Violet Arsenic Phosphorus: Switching p-Type into High Performance n-Type Semiconductor by Arsenic Substitution

Abstract Violet phosphorus, a recently explored layered elemental semiconductor, has attracted much attention due to its unique photoelectric, mechanical properties, and high hole mobility. Herein, violet arsenic phosphorus has for the first time been synthesized by a molten lead method. The crystal structure of violet arsenic phosphorus (P 83.4 As 0.6 , CSD-2408761) was determined by single crystal X-ray diffraction to have similar structure as that of violet phosphorus, where P12 is occupied by arsenic/phosphorus (As/P) atoms as mixed occupancy sites As1/P12. The arsenic substitution has been demonstrated to tune the band structure of violet phosphorus, switching p-type of violet phosphorus to high-performance n-type violet arsenic phosphorus. The effective electron mass along the < 010 > direction is significantly reduced from 1.792 to 0.515 m 0 by arsenic substitution, resulting in an extremely high electron mobility of 2622.503 cm 2 V⁻ 1 s⁻ 1 . The field effect transistor built with P 83.4 As 0.6 nanosheets was measured to have a high electron mobility (137.06 cm 2 V⁻ 1 s⁻ 1 , 61.2 nm), even under ambient conditions for 5 h, much higher than the hole mobility of violet phosphorene nanosheets (4.07 cm 2 V⁻ 1 s⁻ 1 , 73.3 nm). This work provides a new idea for designing phosphorus-based materials for field effect transistors, giving significant potential in complementary metal–oxide–semiconductor applications.