Sequential δ/γ interfacial degradation induces a sigmoidal kinetic transition in stress corrosion cracking during superlong-term thermal aging of duplex stainless steel

Acta Materialia 2026

View at publisher

Authors: Jiamei Wang, Yuhao Zhou, Tianyu Zhu, Yule Wu, Cheng Peng, Xiaoqin Zeng, Zhao Shen, Lefu Zhang, Kai Chen

DOI: 10.1016/j.actamat.2026.122314

Cited by: 47

References: 92

Fields of Study & Subjects

Hydrogen embrittlement and corrosion behaviors in metals High Temperature Alloys and Creep Fatigue and fracture mechanics