The contribution of nitrogen Frenkel-pair formation to the high-temperature heat capacity of uranium mononitride

The high-temperature heat capacity of uranium mononitride (UN) remains uncertain due to conflicting measurements and models above ∼ 1700 K. To assess whether intrinsic defect formation contributes to the observed superlinear behavior of C P ( T ) , we perform large-scale molecular dynamics simulations using two interatomic potentials to quantify nitrogen diffusion and Frenkel-pair populations from 1800–2600 K. Both models show increasing anion mobility, but the Tseplyaev potential yields substantially larger Frenkel concentrations, producing a defect heat-capacity contribution of up to ∼ 10 J/(mol-K). This defect-driven term contributes to the nonlinear high-temperature response, suggesting that nitrogen sublattice disorder provides a plausible intrinsic mechanism for part of the heat-capacity increase in UN.