The structure, composition, and performance impact of a YSZ-GDC interdiffusion layer in solid oxide electrolysis cells

This study provides a combined experimental and computational investigation into the structure and impact of the cation interdiffusion layer that appears at the gadolinium doped ceria (GDC)/yttria stabilized zirconia (YSZ) interface in solid oxide electrolysis cells (SOECs). Scanning transmission electron microscopy (STEM) illustrates that a ∼0.4 μm interdiffusion layer (IDL) with an intermixed cation distribution and fine grain size forms upon sintering. STEM identifies that the interdiffusion layer exists in the cubic fluorite structure despite changes in cation composition. The interdiffusion layer microstructure formed during sintering does not change during SOEC testing at either 1.3V or heightened voltage pulse testing. Modeling predicts that ionic conductivity may decrease in the interdiffusion layer due to Coulombic trapping between mobile oxygen vacancies and excess Gd 3+ acceptor dopants. Yet, the density and continuous nature of the layer should benefit cell stability by substantially reducing the formation of SrZrO 3 , which is corroborated by STEM and Synchrotron X-ray diffraction (XRD). We conclude that the interdiffusion layer acts as a beneficial barrier to Sr diffusion, when operating in a regime where electrolyte void formation is not observed. • Interdiffusion of GDC and YSZ creates continuous IDL with dense microstructure. • Modeling suggests GDC/YSZ interdiffusion layer decreases oxygen ion conductivity. • IDL inhibits formation of insulating phases that degrade electrolysis performance. • IDL contains high total dopant concentrations relative to surrounding YSZ and GDC. • IDL balances the reduction in insulting phase formation with lower O 2− conductivity.