Effect of Impurities on Direct Recycling of Spent LiNi x Co y Mn z O 2 Cathode Material for Lithium-Ion Batteries

Direct recycling is a promising approach for valorizing spent lithium-ion batteries, yet the effect of impurities on cathode regeneration has been insufficiently explored. Herein, an end-of-life LiNi 0.6 Co 0.2 Mn 0.2 O 2 (NCM622) pouch cell is used as a model system to systematically investigate the behavior of impurities and the outcomes for regeneration, using XPS, SRD, and XAS techniques. The analysis identifies AlPO 4, AlF 3, Li 3 PO 4, LiF, Li x PF y O 4, and Li 2 CO 3 as the main impurities in the spent powder, along with Al-inclusion limited to a surface near region. Among these, Al- and F-containing species are found to significantly affect the regeneration process, inducing further Al- and F-inclusion in the regenerated material, while PO 4 3– species exhibit a minimal structural impact. In-depth structural analysis reveals that F-inclusion proceeds via substitution of lattice oxygen, causing increased structural disorder. Al-inclusion most likely involves epitaxial crystal growth promoted by excess lithium salts, resulting in structural asymmetry at elevated inclusion levels. Electrochemical evaluation shows that low-level impurity inclusion has a negligible effect on initial capacity. Yet, impurity accumulation, potentially amplified over repeated recycling, markedly compromises capacity recovery and structural integrity. This work clarifies impurity-induced effects during regeneration and highlights the importance of impurity control for enabling sustainable and effective direct recycling.