Toward the performance assessment of advanced nuclear waste forms: temperature dependence of lanthanide borosilicate glass dissolution

Abstract Lanthanide borosilicate (LaBS) glasses are among the most promising waste forms for the immobilization of high-level radioactive waste generated from advanced nuclear fuel cycles. However, the temperature dependence of their dissolution kinetics remains poorly understood and constrained, limiting the integration of these materials into established performance assessment models. Here, we investigate the dissolution behavior of the legacy AmCm2-19 LaBS glass and the benchmark alkali aluminoborosilicate ISG-1 in deionized water between 50 °C and 250 °C using ASTM C1285 (Product Consistency Test-B) protocols. For AmCm2-19 LaBS glass, normalized elemental release rates for boron and silicon increase with temperature before plateauing near 150 °C, consistent with solubility-limited behavior. From data obtained at 50 °C and 100 °C, Arrhenius analysis yields activation energies of E a (B) = 24.8 ± 0.3 kJ mol⁻¹ and E a (Si) = 14.4 ± 0.2 kJ mol⁻¹, similar or slightly lower than those previously reported for two other compositions of LaBS glasses. No secondary phases or alteration layers were detected by SEM-EDX or pXRD. These results establish one of the first temperature-dependent kinetic datasets for LaBS glass dissolution, providing quantitative parameters to inform mechanistic corrosion models and predictive simulations of glass degradation in geological disposal environments.