Improving protonic ceramic electrochemical cell performance via a dual-phase reaction-sintered bilayer electrolyte

Abstract Protonic ceramic electrochemical cells (PCCs) are promising energy conversion devices, but their fabrication remains challenging. In particular, the typical electrolytes for PCCs such as BaCe 0.7 Zr 0.1 Y 0.1 Yb 0.1 O 3− δ (7111) and BaCe 0.4 Zr 0.4 Y 0.1 Yb 0.1 O 3− δ (4411) suffer from intrinsic barium evaporation issues during high-temperature sintering. This tendency towards barium loss, combined with their highly refractory nature, leads to a tradeoff between sinterability and chemical stability. To address this tradeoff, we propose a bilayer electrolyte combining layers of 4411 and 7111 materials that is designed to enhance sinterability and conductivity through dual-phase reactive sintering. Our findings demonstrate that the bilayer structure exhibits shrinkage behavior closely matched to that of the fuel electrode substrate, with a higher shrinkage compared to a single-layer 4411 electrolyte. Utilizing this bilayer electrolyte structure, our PCCs achieve a peak power density of 637 mW∙cm −2 in fuel-cell mode and a current density of 1060 mA∙cm −2 at 1.3 V in electrolysis mode at 600 °C. Our PCCs demonstrate high Faradaic efficiency of 83% at 1.3 V and 500 °C. Hybrid distribution of relaxation times (DRT) polarization mapping further reveals that the bilayer structure reduces Ohmic and polarization resistance in both fuel-cell and electrolysis modes.