Incommensurately modulated structures of the M 1/8 Pr 5/8 MoO 4 ( M = Li, Na, K) scheelites

The effect of cation substitutions in the scheelite-type framework is investigated to understand the ordering of M + /Pr 3+ cations and vacancies in the structure. The cation deficient M 1/8 Pr 5/8 □ 1/4 MoO 4 ( M = Li, Na, K) phases were synthesized using solid state reactions. The K:Pr ratio in the K 1/8 Pr 5/8 MoO 4 sample was determined by inductively coupled plasma mass spectroscopy, inductively coupled plasma optical emission spectrometry and total reflection X-ray fluorescence spectroscopy. The local element distributions in K 1/8 Pr 5/8 □ 1/4 MoO 4 were determined by energy-dispersive X-ray spectrometry. The incommensurately modulated crystal structures of the scheelite-based M 1/8 Pr 5/8 MoO 4 ( M = Li, Na, K) phases were refined from synchrotron powder X-ray diffraction data. The analysis revealed that cation ordering in the M 1/8 Pr 5/8 MoO 4 ( M = Li, Na) structures is incomplete and is more accurately described by continuous, rather than discontinuous (step-like), occupational modulation functions. The occupancy modulation waves for Li/Na and Pr atoms demonstrate an antiphase relation. Compared with M = Li, Na, the order of K and Pr cations in the A position in the K 1/8 Pr 5/8 MoO 4 structure is best approximated by crenel functions. Refining the coordinates and lengths of three atomic domains yields the composition of K 0.145 Pr 0.618 MoO 4 . In all cases, the modulation arises from ordering of M /Pr cations and cation vacancies at the A -sublattice of the parent scheelite AB O 4 structure. The distortion of PrO 8 and M O 8 polyhedra is practically independent of the radius of the M + cations. The refinements of the M 1/8 Pr 5/8 MoO 4 ( M = Li, Na, K) structures reveal that MoO 4 2− tetrahedra in these scheelite-type compounds demonstrate a flexible geometry. Both Mo—O bond distances and O—Mo—O bond angles vary significantly with changing the population of the A site by cations with different sizes.