Improving perovskite solar module stability by understanding and mitigating scribe-induced chemo-thermomechanical degradation

Recognizing the correlation between the design of perovskite solar module (PSM) and their degradation mechanisms under environmental stressors helps to enable their long- term reliability. This work reports on the impact of the hole-transport layer (HTL) on thermal cyclability and degradation mechanisms of p-i-n PSMs by comparing 3 HTLs: NiOx , MeO-2PACz (a self-assembled monolayer), and a bilayer HTL of MeO-2PACz on NiOx . We observe surprising thermal cyclability from a performance standpoint despite generating clear degradation products. We find that without a fully dense HTL, seemingly insignificant moisture/oxygen ingress through the edge of the PSMs can lead to rapid destabilization of the metal halide perovskite (MHP) layer due to reactions between MHP degradation byproducts and the indium-tin oxide layer. We also show that illumination-induced cation phase segregation is dependent on the presence of an inactive area (regions of the substrate uncovered by the top electrode). As such, we find that a dense interface between the MHP and ITO is necessary for chemically robust PSMs and highlight criteria for testing field-relevant configurations in lab-scale architectures.