In Situ Li Seed Formation Enables Uniform Plating in Anode-Free Solid-State Batteries

Anode-free solid-state batteries (AFSSBs) are a promising route toward achieving high energy density. In these cells, the anode contains no pre-stored lithium (Li). Instead, all Li inventory originates from the cathode and is freshly deposited onto a bare current collector during charging. However, achieving uniform and defect-free Li plating on this bare current collector remains a major challenging, often resulting in low Li plating/stripping efficiency and rapid capacity decay. Here, for the first time, operando neutron imaging is employed to visualize Li plating/stripping behavior in an anode-free full cell with LiNi0.82Mn0.07Co0.11O2 (NMC) as the cathode. Operando measurements reveal that complete stripping of Li leaves isolated Li residues on the current collector, which degrades interfacial contact between the current collector and solid-state electrolyte. To mitigate this interfacial issue and promote more uniform Li deposition, we implement a discharge cutoff voltage strategy that intentionally retains a thin residual Li layer after stripping. This thin Li layer, serving as an in situ–formed seed layer, not only enables more homogeneous subsequent Li plating but also improves interfacial contact. As a result, the anode-free cell with a controlled discharge voltage of 3.5 V exhibits excellent long-term cycling stability, maintaining a discharge capacity of 116 mAh g-1 with a retention rate of 83.4% and an average Coulombic efficiency of approximately 99.9% after 430 cycles at 0.25 C. In contrast, the cell with a conventional discharge cutoff voltage of 2.8 V exhibits rapid capacity decay, retaining only 59.7 mAh g-1 after 50 cycles with a capacity retention of 40.7%. This work offers a practical strategy to unlock the long-term viability of anode-free solid-state batteries.