Investigation of Fracture Process of Q245R During Single Edge Notched Tension Test with Acoustic Emission

Acoustic emission (AE) technology, a kind of non-destructive testing method, was used in this study to monitor the fracture process of Q245R steel in the single edge notched tension (SENT) test. The obtained AE signals were first processed by the sensor gauge method to distinguish the noise and signals related to a fracture. Based on the filtered data, it was found that the load-displacement curve and load–Crack Mouth Opening Distance (CMOD) curve of the fracture development were correlated with the characteristics of signals. In addition, an AE crack development index (CDI) was proposed to characterize different stages in the crack propagation process, and the results were verified by unloading compliance experiments. The results showed that the condition of structure can be well characterized by trends of cumulative counts and peak amplitudes of AE signals. In addition, stable cracks were found to occur when the load reached 92% of the ultimate load which produced AE signals with high counts, duration, and more high-amplitude signals. The proposed AE CDI of 40%max(CDI), 50%max(CDI), and 60%max(CDI) reflects the elastic, plastic, and stable crack propagation stages under monotonic tension, respectively, and remains stable even when the tensile loading method changes.