The Impact of Oil Shale Ash on the Mechanical Properties of Cement Mortar as a Partial Cement Substitute for Sustainable Buildings

This research intends to investigate and analyze the usage of Jordanian oil shale ash (OSA) as a replacement material for ordinary Portland cement and pozzolanic cement in mortar. To start, oil shale was collected from the Wadi Al-Shallala location, crushed, sieved and burned at 800 °C for 24 h. OSA partially replaced the ordinary Portland and pozzolanic cements with ratios of 10%, 20%, and 30%. This research looked into the effect of cement substitution on the standard consistency and hardening time for cement paste. The water contents as well as beginning and final hardening times increased due to the higher replacement ratios of the cements. Also, pozzolanic activity index (PAI) along with scanning electron microscope (SEM), energy dispersive X-ray spectroscopy (EDX) testing and mechanical properties (compressive and flexural strengths) of mortar with both types of cement substitution were evaluated. The compressive strength and flexural strength were checked following 3, 7, 14, 28, 56 and 90 days of curing, while (SEM) was conducted just at 28 days old with a 20% replacement ratio in mortar specimens. Results show that 20% OSA substitution for ordinary Portland cement or Pozzolanic cement raises compressive strength and flexural strength, plus provides better morphology. Thus, oil shale is seen as a natural pozzolanic material that increases efficiency in cement mixtures.