Hierarchical In2MnS4 Flower-like Architectures for Efficient Dye Degradation and Methanol Oxidation

Hierarchical In2MnS4 microflowers were synthesized via a hydrothermal approach and evaluated as multifunctional photo-/electrocatalysts for crystal violet (CV) dye degradation and methanol oxidation. The synthesis strategy produced three-dimensional flower-like architectures composed of nanoscale subunits with high crystallinity and uniform elemental distribution. Optical characterization revealed strong visible-light absorption with a bandgap of approximately 1.74 eV, indicating suitability for solar-driven photocatalysis. In2MnS4 microflowers achieved 96.6% degradation of CV dye within 100 min, whereas negligible activity was observed without the catalyst. Kinetic analysis followed a pseudo-first-order model with an apparent rate constant of 0.029 min−1. The catalyst maintained stable performance over four consecutive cycles, confirming good recyclability. Photoelectrochemical measurements showed a stable photocurrent response and reduced charge-transfer resistance, indicating efficient separation and transport of photogenerated charge carriers. Furthermore, electrochemical measurements revealed increased anodic responses and sustained current behavior in the presence of methanol, suggesting an electrochemical response upon methanol addition. These results highlight In2MnS4 microflowers as promising visible-light-responsive materials for environmental remediation and energy-related catalytic applications.