Thiol-Ene Crosslinking of Polysiloxane Networks on Cotton for Durable Hydrophobic Finishes

Cotton fabrics are widely used due to their comfort and biodegradability; however, their intrinsic hydrophilicity limits their performance in advanced applications. In this work, a fluorine-free approach for imparting durable hydrophobicity to cotton was developed based on thiol-ene crosslinking of polysiloxane networks formed on the fiber surface. Two thiol-functional polysiloxanes differing in –SH group content were combined with four vinyl-functional organosilicon crosslinkers under UV (2,2-dimethoxy-2-phenylacetophenone (DMPA)) and thermal (2,2′-azobis(2-methylpropionitrile) (AIBN)) initiation. FT-IR analysis confirmed the presence of siloxane structures, while SEM-EDS revealed stable silicon- and sulfur-containing layers. SEM observations showed continuous coatings without blocking the textile structure. Water contact angle (WCA) measurements demonstrated that hydrophobic performance strongly depends on thiol content and crosslinker structure, with the highest values obtained for the thiol-rich polysiloxane and tetrafunctional vinyl crosslinker. All modified fabrics exhibited high durability, with minimal changes in WCA and complete droplet stability (1800 s) after washing. In the case of the lower-functionality polysiloxane, an increase in hydrophobicity after washing was observed, attributed to the reorganization of siloxane chains. These results demonstrate that thiol-ene crosslinking provides an effective strategy for designing durable, fluorine-free hydrophobic coatings on cotton.