Effect of Inclined Angles and Contouring Parameters on Upskin Surface Characteristics of Parts Made by Laser Powder-Bed Fusion

Surface finish plays a critical role in the tribological performance of additively manufactured engineering components. In exploring part characteristics in laser powder-bed fusion (L-PBF), this study investigates the effect of contouring strategies on the upskin surface of inclined specimens (30°, 45°, and 60°) made with L-PBF, using post- and pre-contouring strategies with various levels of process parameters. The surface data of fabricated inclined specimens were acquired by white-light interferometry, followed by a quantitative analysis using surface images. The results show that post-contouring leads to better surface finishes, with the lowest Sa of 8.68 µm attained at the highest laser power (195 W) and the slowest scan speed (500 mm/s) on 30°-inclined specimens, likely due to increased remelting and less step-edges. In contrast, pre-contouring produces distinct surface textures on the upskin of L-PBF specimens, resulting in a rougher surface morphology, with a maximum Sa of 33.39 µm also from 30°-inclined specimens at the lowest power (100 W) and the highest speed (2000 mm/s), suggesting an insufficient remelting of surface defects. In comparative analysis, in general, post-contouring yields smoother upskin surfaces, with a 17%–30% reduction in Sa, than those from equivalent pre-contouring conditions, highlighting the potential of scan sequences for optimizing L-PBF to improve the surface finish of inclined structures.