Simulation and Monitoring of Interfacial Microcracks Between Ultra-Weak Fiber Bragg Grating Sensor and Asphalt Mixture

The precision of data gathered from Ultra-Weak Fiber Bragg Grating (UWFBG) sensing technology is limited when measuring strain within asphalt pavements. To better understand its measurement mechanism and correct possible errors, this study examines the synergy deformation behavior between UWFBG and asphalt mixtures under loads. Initially, the mesoscopic model of asphalt mixture containing UWFBG was constructed using a discrete element model, followed by the validation of the model. Then, the propagation of microcracks at the interface between the asphalt mixture and UWFBG was analyzed, revealing damage characteristics of this material under various loading stages. Additionally, a quantitative relationship between the crack width and the monitoring strain was identified. The significant effect of introducing the sensor on crack propagation and interface debonding in strain response was also highlighted. The results indicate that when displacement exceeds 1.4 mm during a bending test, the number of both damage and microcracks increases markedly, with cracks progressively developing. Especially at the UWFBG interface subjected to a tensile load, microcrack growth rises sharply, leading to the failure of the interface. The mor-UWFBG interface is not the main damage location, but it is the most vulnerable location to damage and may be the one affecting the monitoring of UWFBG. Without sensors, a consistent linear relationship between monitoring strain and crack width is observed within the asphalt mixture. After introducing the UWFBG sensor, the strain-crack response of the asphalt mixture is divided into three stages: crack initiation, crack propagation, and interface debonding. When the crack width surpasses 0.03 mm, interface debonding significantly influences the strain growth rate, indicating the necessity of correcting the synergy deformation.