Experimental Investigation of the Effects of Silver and Copper Content on the Fluidity of Biodegradable Zinc Alloys

Ag and Cu in biodegradable Zn alloys have been the focus of research due to their biocompatible corrosion products, as well as their ability to improve the mechanical properties of the alloy. In this research, the impact of Ag and Cu on the fluidity of biodegradable Zn alloys was evaluated through the spiral fluidity test. Zn–xAg and Zn–xCu alloys containing Ag or Cu in pure Zn at proportions of 0.5, 1, 2, and 3 wt.% were prepared. In the first stage of the study, the casting temperature to be used in the fluidity tests of the alloys was determined by casting pure Zn at different temperatures. Spiral castings of the alloys were then produced and the fluidity lengths in the spiral channel were measured. Test results showed that the mold filling distances decreased with increasing amounts of Ag and Cu, with Cu causing a stronger reduction than Ag at comparable addition levels. When the Ag content in Zn was raised from 0.5 wt.% to 1 wt.%, a significant reduction in fluidity was observed. Formation of CuZn5 and ε–AgZn3 phases in the microstructures was identified as the main factor limiting melt flow. These findings provide insights into how Ag and Cu additions influence the castability of Zn alloys, offering guidance for optimizing alloy composition for biodegradable implant applications.