Effects of Al and O Concentrations on the Practical Properties of TiAl4822 for Jet Engine Blades and the Feasibility of Machining Chip Reuse

Maintaining a consistent quality of TiAl4822 blades used in jet engines is crucial, even when compositional variations occur during production. This study investigates the optimal Al and O concentration ranges that yield favorable practical properties. Additionally, the feasibility of reusing machining chips as a low-cost melting feedstock is explored. The results indicate that both impact resistance at 25 °C and machinability remain unaffected or even improve at O concentrations up to at least 0.13 wt%. Moreover, materials containing 0.13 wt% O exhibit the widest optimal range of Al concentrations (46.8–47.4 at%), but was narrower at lower or higher Al concentrations. The influence of the α2-phase ratio on impact resistance is substantially greater than that of O concentration, with the optimal range being 0.2–0.3. Furthermore, a new pre-treatment method is developed to reuse machining chips containing large amounts of water-soluble cutting oil. This method involves removing C through atmospheric heating after ultrasonic cleaning using acetone. Furthermore, TiAl4822 castings including these preprocessed chips exhibit superior properties compared with those of chip-free low-O materials, despite the higher O concentration. These findings demonstrate that moderate O enrichment is tolerable, and even beneficial, enabling cost-effective recycling in TiAl4822 blade production.