Characterization of Novel Composite Scintillators Based on the Epitaxial Structures of TbAG:Ce/GAGG:Ce and TbAG:Ce,Mg/GAGG:Ce Garnets in Mixed Radiation Fields

In this work, we present a study of newly developed two-layered composite scintillators based on epitaxial structures of garnet compounds for the simultaneous registration of different components of mixed radiation fluxes, and we evaluate their α/β/γ discrimination performance. The composite scintillators under study were doubly layered structures composed of TbAG:Ce or TbAG:Ce,Mg single-crystalline film grown onto Czochralski-grown GAGG:Ce single-crystal substrates using the liquid-phase epitaxy (LPE) method. The spectrometry measurements were performed with four different radioactive sources: 137Cs (emitting 661.6-keV γ rays), 241Am (5.5-MeV α particles and 59.5-keV γ rays), 90Sr (β particles with energies up to 2 MeV), and 14C (β particles with energies up to 156 keV). The pulse-height spectra (PHS) were recorded with a shaping time of 10 μs in an amplifier due to the presence of long scintillation components in the tested samples. Scintillation time profiles were measured under excitation of 661.6-keV γ rays, 5.5-MeV α particles, and β particles from 90Sr/90Y and 14C. Both types of TbAG:Ce film/GAGG:Ce substrate and TbAG:Ce,Mg film/GAGG:Ce substrate composites show good ability for the simultaneous registration of the mentioned components in the mixed radiation field with very reasonable Figure-of-Merit values: FoM(τ) greater than 0.2 and FoM(PSD) greater than 1.0.