Influence of Fire Retardant Treatment, Humidity Changes and UV Exposure on the Color Changes of Scots Pine (Pinus sylvestris L.) Wood for Visible Building Applications

Glued-laminated timber (GLT) and cross-laminated timber (CLT) panels are increasingly used as exposed structural elements in representative buildings. These structures are often part of public-use areas, which require the application of restrictive fire-safety measures without significantly affecting the color of exposed wooden surfaces during the service life of these building elements. The effect of fire-retardant treatments on the color of Scots pine (Pinus sylvestris L.) wood was evaluated using five impregnation agents with different active substances. Changes in gloss and color characteristics—lightness (L*), green-red coordinate (a*), and blue-and-yellow coordinate (b*)—were measured sequentially directly after impregnation, after exposure to variable humidity conditions and after exposure to UV radiation. The total color difference (ΔE*) ranged from 2.82 to 17.76 after impregnation and increased to 6.31–20.71 after aging, indicating a risk of aesthetic deterioration of fire-retardant-treated wood surfaces under typical service conditions for timber structures in representative buildings. The most pronounced color changes were observed for the fire retardant containing potassium and copper compounds (FR4) and the combination of 2-aminoethanol with boric acid (FR5).