Acoustic and Mechanical Performance of Treated Rubber–Concrete Composites for Soundproofing in Wind Power Applications

The current study examines the innovative use of rubber–concrete composites as structural solutions that provide significantly higher noise absorption properties compared to traditional concrete. Focusing on their potential for sound insulation in challenging environments such as wind energy infrastructure, the study examines the effect of varying contents of ground tyre rubber (GTR) content (20%, 40%, and 60% by volume) and acetone treatment duration (0, 1, 6, and 24 h) on the characteristics of the composite. The results demonstrate that these rubber–concrete composites significantly improve both sound absorption and sound insulation. An increase in sound absorption coefficients to approximately 0.18 was observed, representing an average improvement of 43.4% compared to the average coefficient of the reference mixture, 0.043. This improvement is particularly effective in the 100–1250 Hz frequency range and maintains stable properties from 50 to 1600 Hz. Sound transmission losses also showed a clear improvement in the mid-frequency ranges. Despite their excellent acoustic characteristics, these structural composites demonstrate a compromise in mechanical properties. Compressive strength decreased from approximately 43–46 MPa (control) to 25–38 MPa at 60% rubber content after 28 days, representing a 40–46% reduction. The reduction in flexural strength was even more pronounced, decreasing by approximately 60% at a rubber content of 35%. However, treatment of GTR with acetone significantly improved interfacial bonding, increasing mechanical integrity at moderate rubber doses (20–40%). The optimal range of rubber content, providing a balance between acoustic benefits and structural integrity, appears to be 15–25%.