Influence of Welding Control Mode on the Joint Performance of Ultrasonically Welded Carbon Fiber-Reinforced Polycarbonate

Carbon fiber-reinforced thermoplastic (CFRTP) composites are now widely used in many fields. Ultrasonic welding (UW) is a key technology for joining these materials. The control mode of UW has a great effect on the quality of the welded joints. However, there is still not enough research comparing the different welding control modes. This paper investigates the effects of the time control, energy control, and displacement control modes on the ultrasonic welding quality of carbon fiber-reinforced polycarbonate (CF/PC). A flat PC film is used as the energy director (ED). The evaluation focuses on the lap-shear strength (LSS), macro- and micro-morphology, fracture surface characteristics and power-displacement curves of the welding process. Furthermore, significant differences are observed in the temperature field evolution and joint failure modes across the different control modes and process parameters. Results indicate that the displacement control mode achieves the highest joint quality and process stability, yielding a maximum LSS of 30.6 MPa. A correlation analysis reveals that the displacement-energy relationship exhibits the strongest coupling, and the Pearson correlation coefficient r is 0.896.