Creep Behavior of Inconel 718 Produced by Laser Powder Bed Fusion (LPBF)

Additive manufacturing using laser powder bed fusion (LPBF) has been widely used to produce nickel-based superalloy components with complex shapes for high-temperature applications requiring creep resistance. In this research, the creep behavior of LPBF Inconel 718 under solution and double-aging heat treatments, performed at 590–650 °C under stresses of 450–550 MPa, is studied. The characterization included optical microscopy, scanning electron microscopy (SEM), porosity analysis, Vickers microhardness tests, and fracture surface examination. The findings revealed that even after heat treatment, the material maintained a mainly directional, columnar microstructure, with an average porosity below 1%, which was unevenly distributed and contained critical defects related to lack-of-fusion (LOF) and trapped powder. Fracture after creep presents regions of ductile failure alongside facets indicative of quasi-cleavage. Kinetic analysis revealed a high stress exponent (n = 18.26) and an activation energy (Qc = 410–538 kJ/mol), indicating that the deformation operates within the power-law breakdown (PLB) regime, where dislocation–precipitate interactions govern the creep rate in this precipitation-strengthened superalloy. Overall, the results highlight that the directional microstructure and residual defects typical of LPBF can reduce the creep resistance of Inconel 718, underscoring the importance of post-processing methods and internal defect control specifically tailored for additively manufactured materials.