Effect of Radiation up to 30 MGy on Mechanical and Dielectric Properties of Polymers for Superconducting and Resistive Magnets

The effect of ionising irradiation up to 30 MGy on the mechanical and dielectric properties of different polymers for potential use in particle accelerators and detectors was compared in this study. The materials studied include the high-performance polymers PEEK, PPS and PEI; pure anhydride- and amine-based epoxy resin systems for coil impregnation and adhesive bonding; glass fibre epoxy composites; and FDM, SLA and SLS 3D-printed materials and polyurethanes. Gamma irradiation was applied in ambient air at an approximate dose rate of 2 kGy/h. Dose-dependent radiation damage was monitored by three-point bending tests, Shore A hardness, tensile stress-strain measurements and breakdown voltage tests in liquid nitrogen. Radiation hardness was rated according to two criteria: the dose at which the initial mechanical strength is halved and the dose at which the mechanical strength is reduced below a certain threshold value. The degradation of the breakdown voltage was preceded by the degradation of mechanical properties.