Experimental Investigation of Hot Drilling and Their Effect on the Damage Mechanisms in CFRP Nanocomposites

Carbon fiber-reinforced polymer (CFRP) composites modified with alumina (Al2O3) and silicon carbide (SiC) nanoparticles were developed to produce hybrid nanocomposites with improved mechanical and thermal characteristics. This study investigates the hot drilling behavior of unidirectional CFRP and hybrid nanocomposites by examining the effects of spindle speed, feed rate, drill diameter, and drill geometry (step, core, and twist). Response Surface Methodology (RSM) and Analysis of Variance (ANOVA) were used to identify the most influential parameters governing drilling-induced damage. ANOVA results revealed that drill geometry was the most dominant factor, contributing more than 89% to delamination, burr formation, and surface roughness, followed by drill diameter with over 7% contribution. For temperature rise, drill geometry accounted for more than 50% of the total variation, while drill diameter contributed over 17%. Among the tools evaluated, the step drill produced the minimum drilling-induced damage, followed by the twist drill. In terms of material performance, the Al2O3-reinforced hybrid nanocomposite exhibited superior drilling behavior compared to the SiC-reinforced and neat CFRP laminates. Overall, the results demonstrate that drilling-induced damage under hot drilling conditions can be effectively minimized through appropriate selection of tool geometry and process parameters, confirming the suitability of hot drilling for machining aerospace-grade CFRP hybrid nanocomposites.