Assessment of Geometric Scaling Factors and Anisotropic Phase Formation in GMAW-Additively Manufactured Duplex Stainless Steel (ER2209) Components

Duplex stainless steel (DSS) blends impressive mechanical and chemical characteristics to withstand aggressive environments. Its fabrication by Gas Metal Arc Welding-Additive Manufacturing is an emerging research topic. However, its sensitive grain structure and alloy composition are prone to deterioration by repeated thermal shocks. Whether optimal weld parameters can resolve these challenges without additional costs from special fillers, gases, or mechanisms is a valid question. In this study, how different wire feed speeds, travel speeds, and weld voltages, chosen from a set of preliminary beads, translate into wall dimensions, phase formation and distribution, morphological transformation, and elemental segregation is investigated. The unique DSS microstructures were characterised using scanning electron microscopy and energy-dispersive spectroscopy to reveal differences in microstructural evolution and ferrite-austenite (α-γ) structure. The deposited walls exhibited satisfactory geometric quality with negligible distortions. However, the height suppression was noticeable at the deposition energy (DE) of 755 J/mm. Metallographic analysis revealed low γ phase formation (70%) in the high DE wall (755 J/mm). The parameters WFS:TS = 15, TS = 35 cm/min, WFS = 525 cm/min, and V = 20.804 volts suppressed the elemental segregation while maintaining a suitable phase balance without post-processing.