A Hybrid Inorganic–Organic Schiff Base-Functionalised Porous Platform for the Remediation of WEEE Polluted Effluents

An inorganic–organic hybrid nano-adsorbent was prepared by chemical immobilisation of an organic Schiff base Cu (II) ion receptor, DHB ((E)-N-(1-(2-hydroxy-6-methyl-4-oxo-4H-pyran-3-yl) ethylidene) benzohydrazide), a selective dehydroacetic acid-based chemosensor, onto a mesoporous silica support. In order to prepare the sorbent, the silylating agent was anchored onto the silica. During this procedure, 3-Chloropropyl trimethoxy silane (CPTS) was attached to the surface, increasing hydrophobicity. By immobilising DHB onto the CPTS platform, the silica surface was activated, and as a result the coordination chemistry of the Schiff base generated a hybrid adsorbent with the capability to rapidly sequestrate Cu (II) ions from wastewater, as an answer to combat growing Waste Electrical and Electronic Equipment (WEEE) contamination in water supplies, in the wake of a prolonged consumerism mentality and boom in cryptocurrency mining. The produced hybrid materials were characterised by FTIR, proximate and ultimate analysis, nitrogen physisorption, PXRD, SEM, and TEM. The parameters influencing the removal efficiency of the sorbent, including pH, initial metal ion concentration, contact time, and adsorbent dosage, were optimised to achieve enhanced removal efficiency. Under optimal conditions (pH 7.0, adsorbent dosage 3 mg, contact time of 70 min, and 25 °C), Cu (II) ions were quantitatively sequestered from the sample solution; 93.1% of Cu (II) was removed under these conditions. The adsorption was found to follow pseudo-second-order kinetics, and Langmuir model fitting affirmed the monolayer adsorption.